提示信息| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
| 机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO 527 | 490(6,950) | kg/cm2(MPa)[Lb/in2] | |
| 断裂伸长率 | ASTM D638/ISO 527 | - | % | ||
| 拉伸模量 | ASTM D638/ISO 527 | - | kg/cm2(MPa)[Lb/in2] | ||
| 拉伸屈服伸长率(延伸率) | ASTM D638/ISO 527 | 20 | % | ||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | - | % | ||
| 弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 27000(38000) | kg/cm2(MPa)[Lb/in2] | ||
| 弯曲强度 | ASTM D790/ISO 178 | 790(11,660) | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | R-116 | |||
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | |
| 1/4" -30℃ | ASTM D256/ISO 179 | 17(3.1) | kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" 23℃ | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | ||
| 1/8" -30℃ | ASTM D256/ISO 179 | 20(3.7) | kg·cm/cm(J/M)ft·lb/in | ||
| Charpy冲击强度 | 23℃ （缺口） | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | |
| -30℃（缺口） | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | ||
| 23℃（无缺口） | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | ||
| -30℃（无缺口） | ASTM D256/ISO 179 | - | kg·cm/cm(J/M)ft·lb/in | ||
| 物性性能 | 比重（密度） | ASTM D792/ISO 1183 | 1.05 | ||
| 成型收缩率 | ASTM D955 | - | % | ||
| 熔融指数（流动系数） | 200℃/5kg | ASTM D1238/ISO 1133 | 1.6 | g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 | 22 | g/10min | ||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | - | % | ||
| 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | 99(210) | ℃（℉） |
| 未退火 | ASTM D648/ISO 75 | 88(190) | ℃（℉） | ||
| 维卡软化点 | ASTM D1525/ISO R306 | 105(221) | ℃（℉） | ||
| 熔点 | - | - | ℃（℉） | ||
| 燃烧性（率） | UL94 | 1.6mmHB | |||
| 线性膨胀系数 | ASTM D696/ISO 11359 | - | mm/mm.℃ | ||
| 加工条件 | 干燥条件 | 80°C下烘料约2~3小时 | |||
| 加工温度 | 射嘴 | 180~230°C | ℃ | ||
| 料筒前段 | 190~230 | ℃ | |||
| 料筒中段 | 190~230 | ℃ | |||
| 料筒后段 | 180~220 | ℃ | |||
| 熔体温度 | - | ℃ | |||
| 模具温度 | 30~70°C | ℃ | |||
| 压力 | 注塑压力 | - | Mpa | ||
| 保压压力 | - | Mpa | |||
| 背压 | - | Mpa | |||
| 螺杆转速 | - | rpm | |||
| 其他 | 备注 | - | |||
| 颜色 | - | ||||
| 特性 | 高光泽性 高刚性。 | ||||
| 用途 | 电视机前壳 / 复印机外壳 / 电话机壳 / 化妆品盒 / 轮胎盖 | ||||
供应奇美PC-540ABS