hysical	Nominal Value	Unit	Test Method
Specific Gravity	1.21	g/cm3	ASTM D792
Specific Volume	0.830	cm3/g	ASTM D792
Density	1.22	g/cm3	ISO 1183
Melt Mass-Flow Rate (MFR) (250°C/5.0 kg)	16	g/10 min	ISO 1133
Melt Volume-Flow Rate (MVR) (250°C/5.0 kg)	15.0	cm3/10min	ISO 1133
Molding Shrinkage - Flow (3.20 mm)	0.80 to 1.0	%	Internal Method
Molding Shrinkage - Across Flow 2	0.80 to 1.0	%	Internal Method
Water Absorption (Saturation, 23°C)	0.50	%	ISO 62
Water Absorption (Equilibrium, 23°C, 50% RH)	0.15	%	ISO 62
Outdoor Suitability	f2		UL 746C
Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus			ASTM D638
-- 3	2250	MPa
-- 4	2250	MPa
Tensile Modulus	2050	MPa	ISO 527-2/1
Tensile Strength 5 (Yield)	53.0	MPa	ASTM D638
Tensile Stress (Yield)	50.0	MPa	ISO 527-2/50
Tensile Strength 5 (Break)	51.0	MPa	ASTM D638
Tensile Stress (Break)	50.0	MPa	ISO 527-2/50
Tensile Elongation 5 (Yield)	4.0	%	ASTM D638
Tensile Strain (Yield)	4.0	%	ISO 527-2/50
Tensile Elongation 5 (Break)	120	%	ASTM D638
Tensile Strain (Break)	120	%	ISO 527-2/50
Flexural Modulus 6 (50.0 mm Span)	2030	MPa	ASTM D790
Flexural Modulus 7	2000	MPa	ISO 178
Flexural Stress 7, 8	80.0	MPa	ISO 178
Flexural Strength 6 (Yield, 50.0 mm Span)	84.0	MPa	ASTM D790
Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength 9 (23°C)	55	kJ/m2	ISO 179/1eA
Notched Izod Impact			ASTM D256
-40°C	300	J/m
-30°C	530	J/m
23°C	710	J/m
Notched Izod Impact Strength 10			ISO 180/1A
-30°C	30	kJ/m2
23°C	50	kJ/m2
Instrumented Dart Impact (23°C, Total Energy)	60.0	J	ASTM D3763
Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm)	107	°C	ASTM D648
Deflection Temperature Under Load			ASTM D648
1.8 MPa, Unannealed, 3.20 mm	84.0	°C
1.8 MPa, Unannealed, 6.40 mm	99.0	°C
Heat Deflection Temperature 11 (1.8 MPa, Unannealed, 64.0 mm Span)	75.0	°C	ISO 75-2/Af
Vicat Softening Temperature	122	°C	ASTM D1525 12
Vicat Softening Temperature
--	120	°C	ISO 306/B50
--	125	°C	ISO 306/B120
CLTE - Flow (-40 to 40°C)	9.5E-5	cm/cm/°C	ASTM E831
CLTE - Flow (-40 to 40°C)	9.5E-5	cm/cm/°C	ISO 11359-2
CLTE - Transverse (-40 to 40°C)	9.0E-5	cm/cm/°C	ASTM E831
CLTE - Transverse (-40 to 40°C)	9.0E-5	cm/cm/°C	ISO 11359-2
RTI Elec	75.0	°C	UL 746
RTI Imp	75.0	°C	UL 746
RTI Str	75.0	°C	UL 746
Electrical	Nominal Value	Unit	Test Method
Arc Resistance 13	PLC 5		ASTM D495
Comparative Tracking Index (CTI)	PLC 1		UL 746
High Amp Arc Ignition (HAI)	PLC 0		UL 746
High Voltage Arc Tracking Rate (HVTR)	PLC 0		UL 746
Hot-wire Ignition (HWI)	PLC 3		UL 746
Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm)	HB		UL 94

Processing Information
Injection	Nominal Value
Drying Temperature	110
Drying Time	4.0 to 6.0
Drying Time, Maximum	8.0
Suggested Max Moisture	0.020
Suggested Shot Size	50 to 80
Rear Temperature	243 to 266
Middle Temperature	249 to 271
Front Temperature	254 to 277
Nozzle Temperature	254 to 271
Processing (Melt) Temp	260 to 277
Mold Temperature	65.6 to 87.8
Back Pressure	0.345 to 0.689
Screw Speed	50 to 80
Vent Depth	0.013 to 0.020
Extrusion	Nominal Value
Drying Temperature	110 to 116
Drying Time	4.0 to 6.0
Suggested Max Moisture	1.0E-3 to 0.020
Cylinder Zone 1 Temp.	171 to 204
Cylinder Zone 2 Temp.	193 to 254
Cylinder Zone 3 Temp.	204 to 282
Cylinder Zone 4 Temp.	204 to 282
Adapter Temperature	227 to 282
Melt Temperature	243 to 277
Die Temperature	232 to 282
Extrusion Notes
Drying Time (Cumulative): 8 hrs Roll Stack Temp - Bottom: 82 - 93 °C Roll Stack Temp - Middle: 77 - 82 °C Roll Stack Temp - Top: 71 - 82 °C

公司档案

公司名称：	上海同卓新材料容飞工科技有限公司	公司类型：	企业单位 (生产型,贸易型)
所在地：	上海	公司规模：
注册资本：	100万人民币	注册年份：

资料认证：

经营模式：

生产型,贸易型

经营范围：

peek,evoh,lsoh,pa66等各类工程塑料,pi,psu,多晶硅,

主营行业：

代理 / 橡塑代理加盟	仪器仪表 / 橡塑专用仪器仪表	橡塑 / 塑胶容器 / 橡塑垃圾容器
橡塑