Solvay Advanced Polymers AMODEL? AS-4133 HS Polyphthalamide (PPA) Resin, 33% Glass Reinforced, Dry as Molded
AMODEL AS-4133 HS polyphthalamide (PPA), a 33% glass reinforced resin, is one of a new series of PPA resins designed to give high crystallinity when molded in water-cooled molds. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range, low moisture absorption, excellent chemical resistance, and excellent electrical properties.
AMODEL AS-4133 HS resin can be advantageously used for many automotive electrical and electronic applications. These applications may include connectors, sockets, switches, sensors, enclosures, and housings for systems, such as anti-lock brake, traction control, steering, electronic engine control, transmission control, and chassis controls.
This material processes readily on conventional injection molding equipment using water-cooled molds. Its rapid crystallization rate and high flow can result in short cycles and therefore high molding productivity and lower part cost.
Information provided by Solvay Advanced Polymers
Physical Properties | Metric | English | Comments | |
|
||||
Specific Gravity | 1.45 g/cc | 0.0524 lb/in? | ASTM D792 | |
Specific Gravity | 1.45 g/cc | 0.0524 lb/in? | ISO 1183A | |
Moisture Absorption at Equilibrium | 0.29 % | 0.29 % | 24 hours ; ASTM D570 | |
Mechanical Properties |
||||
|
||||
Tensile Strength, Yield | 200 MPa | 29000 psi | ASTM D638 | |
Tensile Strength, Yield at Elevated Temperature | 125 MPa | 18100 psi | 100?C; ISO 527 | |
Tensile Strength, Yield at Elevated Temperature | 211 MPa | 30600 psi | 23?C; ISO 527 | |
Tensile Strength, Yield at Elevated Temperature | 79 MPa | 11500 psi | 175?C; ISO 527 | |
Tensile Strength, Yield at Elevated Temperature | 87 MPa | 12600 psi | 150?C; ISO 527 | |
Elongation at Break at Elevated Temperature | 2.6 % | 2.6 % | 23?C; ISO 527 | |
Elongation at Break at Elevated Temperature | 4.3 % | 4.3 % | 100?C; ISO 527 | |
Elongation at Break at Elevated Temperature | 6.6 % | 6.6 % | 150?C; ISO 527 | |
Elongation at Break at Elevated Temperature | 6.6 % | 6.6 % | 175?C; ISO 527 | |
Elongation at Yield | 2.5 % | 2.5 % | ASTM D638 | |
Tensile Modulus | 11.7 GPa | 1700 ksi | ASTM D638 | |
Tensile Modulus | 12.6 GPa | 1830 ksi | 23?C; ISO 527 | |
Tensile Modulus | 4.8 GPa | 696 ksi | 175?C; ISO 527 | |
Tensile Modulus | 5.3 GPa | 769 ksi | 150?C; ISO 527 | |
Tensile Modulus | 6.8 GPa | 986 ksi | 100?C; ISO 527 | |
Flexural Modulus | 10.4 GPa | 1510 ksi | 23?C; ISO 178 | |
Flexural Modulus | 11 GPa | 1600 ksi | ASTM D790 | |
Flexural Modulus | 4.2 GPa | 609 ksi | 175?C; ISO 178 | |
Flexural Modulus | 4.6 GPa | 667 ksi | 150?C; ISO 178 | |
Flexural Modulus | 7.2 GPa | 1040 ksi | 100?C; ISO 178 | |
Flexural Strength | 100 MPa | 14500 psi | 175?C; ISO 178 | |
Flexural Strength | 111 MPa | 16100 psi | 150?C; ISO 178 | |
Flexural Strength | 176 MPa | 25500 psi | 100?C; ISO 178 | |
Flexural Strength | 290 MPa | 42100 psi | ASTM D790 | |
Flexural Strength | 296 MPa | 42900 psi | 23?C; ISO 178 | |
Poisson's Ratio | 0.41 | 0.41 | ||
Shear Strength | 90 MPa | 13100 psi | ASTM D732 | |
Izod Impact, Notched (ISO) | 9.7 kJ/m? | 4.62 ft-lb/in? | 23?C; ISO 180/1A | |
Izod Impact, Unnotched | 9.61 J/cm | 18 ft-lb/in | ASTM D4812 | |
Izod Impact, Unnotched (ISO) | 59 kJ/m? | 28.1 ft-lb/in? | 23?C; ISO 180/1U | |
Charpy Impact Unnotched | 6.8 J/cm? | 32.4 ft-lb/in? | 23?C; ISO 179/1eU | |
Charpy Impact, Notched | 1.07 J/cm? | 5.09 ft-lb/in? | 23?C; ISO 179/1eA | |
Izod Impact, Notched | 0.8 J/cm | 1.5 ft-lb/in | ASTM D256 | |