点击图片查看大图| 厂家(产地)：韩国锦湖 | 密度：1.04 | 吸水率：0.05 | |
| 牌号：MIB | 类型：标准料 | 成型收缩率：0.45 | |
| 规格级别：其它 | 用途：瓶、杯 | 缺口冲击强度：89.1 | |
| 熔体流动速率：8 | |||
| 查看全部参数> | |||
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 8.0 | g/10min |
| 吸水率 | 24hr | ASTM D-570 | 0.050 | % |
| 比重 | ASTM D-7921.04g/cm3 | |||
| 模具收缩率 | Flow | ASTM D-955 | 0.30-0.60 | % |
| 拉伸屈服强度 | ASTM D-63823.5MPa | |||
| 拉伸屈服伸长率 | ASTM D-63855% | |||
| 弯曲模量 | ASTM D-7902060MPa | |||
| 弯曲屈服强度 | ASTM D-79034.3MPa | |||
| IZOD缺口冲击强度 | 3.18mm | ASTM D-256 | 89.1 | J/m |
| 洛氏硬度 | ASTM D-78568L scale | |||
| 体积电阻率 | ASTM D-2571.0E+16ohm.cm | |||
| 介电强度 | ASTM D-14917.7KV/mm | |||
| 介电常数 | 1E+6Hz | ASTM D-150 | 2.600 | |
| 热变形温度 | 1.80MPa，未退火 | ASTM D-648 | 73.9 | ℃ |
| 维卡软化温度 | ASTM D-152517.7℃ | |||
| 燃烧性 | UL 94HB |