①原料描述部分| 规格级别： | 注塑级 | 外观颜色： | --- |
| 用途概述： | --- |
| 备注说明： | 特性：脱模良好，中粘度 |
②原料技术数据| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 300℃/1.2kg | ASTM D-1238 | 10 | g/10min |
| 吸水率 | 24hr,23℃ | ASTM D-570 | 0.15 | % |
| 平衡吸水率 | 23℃，相对湿度50% | ASTM D-570 | 0.32 | % |
| 物理性能 | 折射率 | --- | ASTM D-542 | 1.586 | --- |
| 透光率 | --- | ASTM D-1003 | 89 | % |
| 雾度 | --- | ASTM D-1003 | 0.7-1.5 | % |
| 模具收缩率 | --- | ASTM D-955 | 0.005-0.007 | in/in |
| 比重 | --- | ASTM D-792 | 1200 | kg/m3 |
| 阻燃等级 | 1.6mm | UL 94 | HB | --- |
| 阻燃等级 | 3.2mm | UL 94 | HB | --- |
| 机械性能 | 弯曲强度 | --- | ASTM D-790 | 96 | MPa |
| 弯曲模量 | --- | ASTM D-790 | 2410 | MPa |
| 缺口冲击强度 | 23℃ | ASTM D-256 | 900 | j/m |
| 冲击强度 | 23℃ | ASTM D-256 | 未破裂 | --- |
| 落锤冲击强度 | 总能量@23℃ | ASTM D-3763 | 87 | J |
| 洛氏硬度 | --- | ASTM D-785 | 118 | R标度 |
| 洛氏硬度 | --- | ASTM D-785 | 73 | M标度 |
| | | | |
| --- | | | |
| 拉伸模量 | --- | ASTM D-638 | 2410 | MPa |
| 电气性能 | 辉光灯丝测试 | 2mm，5s | IEC 695-2-1 | 850 | ℃ |
| 体积电阻 | 23℃，干 | ASTM D-257 | 2.0&tiMES;1017 | Ω.cm |
| 球状压痕温度 | --- | IEC 598-1 | >125 | ℃ |
| 对比电弧径迹指数 | 2mm | IEC 112 | 250 | V |
| 介电强度 | 60Hz | ASTM D-149 | 17 | V/mil |
| 损耗因素 | 60Hz | ASTM D-150 | 0.001 | --- |
| 热 性 能 | 线性热收缩率 | -40℃～82℃ | ASTM D-696 | 68×10-6 | mm/mm/℃ |
| 热变形温度 | 退火@0.45MPa | ASTM D-648 | 144 | ℃ |
| 热变形温度 | 退火@1.82MPa | ASTM D-648 | 141 | ℃ |
| 热变形温度 | 未退火@1.82MPa | ASTM D-648 | 128 | ℃ |
| 维卡软化点 | 50℃/小时，50n重 | ASTM D-1525 | 149 | ℃ |
| 平均燃烧系数 | --- | ASTM D-635 | 25 | mm |
| 其它性能 | 需氧系数 | --- | ASTM D-2863 | 26 | % |