Physical PropertiesMetricEnglishComments Mechanical PropertiesMetricEnglishComments Thermal PropertiesMetricEnglishComments Optical PropertiesMetricEnglishComments

公司长期供应MVLDPE  1012
Density	0.912g/cc	0.0329lb/in3	ExxonMobil Method
Thickness	25.4microns	1.00mil
Melt Flow	1.00g/10 min	1.00g/10 min	ExxonMobil Method
Film Tensile Strength at Yield, MD	7.45MPa	1080psi	at 2% offset; ASTM D882
Film Tensile Strength at Yield, TD	7.38MPa	1070psi	at 2% offset; ASTM D882
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Film Elongation at Break, TD	650 %	650 %	ASTM D882
Puncture Energy	5.84J	4.31ft-lb	Exxon Mobil Method
Elmendorf Tear Strength, MD	8.27g/micron	210g/mil	ASTM D1922
Elmendorf Tear Strength, TD	13.0g/micron	330g/mil	ASTM D1922
Dart Drop	32.3g/micron	820g/mil	ASTM D1709
Film Tensile Strength at Break, MD	71.64MPa	10390psi	ASTM D882
Film Tensile Strength at Break, TD	63.6MPa	9230psi	ASTM D882
1% Secant Modulus, MD	131MPa	19000psi	ASTM D882
1% Secant Modulus, TD	141MPa	20400psi	ASTM D882
Melting Point	116°C	241°F	Peak Melting Temperature; ExxonMobil Method
Haze	16.0 %	16.0 %	ASTM D1003
Gloss	39.0 %	39.0 %	45°; ASTM D2457