AFFINITY™ PL 1880G

Polyolefin Plastomer

陶氏塑料             

       Technical Data                    

产品说明

AFFINITY* PL 1880G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed for use in a variety of demanding packaging applications, including high-speed, form-fill-seal packaging. This resin offers excellent ultimate hot tack strength and low temperature seal initiation, even through contamination in the package.

•     Low seal initiation temperature

•     Excellent hot tack strength

•     High performance sealant layer in flexible packaging

Complies with:                                  

•     U.S. FDA FCN 424                                  

•     U.S. FDA-DMF                                

•     U.S. USP 23                              

•     HPFB No Objection (with limitations)                             

•     EU, No 10/2011                                

•     Japan Hygienic Olefin and Styrene lastics Association              

Consult the regulations for complete detAIls.                     

总体                                         

材料状态      •    已商用：当前有效                    

资料       1    •     Technical Datasheet

搜索UL黄卡     •    陶氏塑料                    

供货地区      •    北美洲   •欧洲          

      •    拉丁美洲      •亚太地区          

机构评级      •     DMF未评级•FDA FCN 424   •JHOSPA未评级      

      •     EU No 10/2011     •HPFB (加拿大) No Objection  •USP 23      

形式             •    颗粒料                 

加工方法      •    吹塑薄膜                    

      物理性能      额定值单位制      测试方法

      比重       0.902g/cm⊃3;    ASTM D792

      熔流率(190°C/2.16 kg)     1.0g/10 min    ASTM D1238

      薄膜      额定值单位制      测试方法

      薄膜厚度-经测试      51µm     

      膜刺穿强度(51 µm)    8.81J      Internal Method

      膜刺穿力(51 µm) 92.5N     Internal Method

      膜耐刺穿性(51 µm)    22.3J/cm⊃3;      Internal Method

      割线模量              ASTM D882

       2%正割, MD: 51 µm   91.7MPa

       2%正割, TD: 51 µm    92.4MPa

      抗张强度              ASTM D882

       MD:屈服, 51 µm  7.24MPa

       TD:屈服, 51 µm   6.89MPa

       MD:断裂, 51 µm  58.6MPa

       TD:断裂, 51 µm   44.7MPa

      伸长率           ASTM D882

       MD:断裂, 51 µm  620%     

       TD:断裂, 51 µm   630%     

      落锤冲击(51 µm) > 830g    ASTM D1709B

      埃尔曼多夫抗撕强度3              ASTM D1922

       MD: 51 µm    550g      

       TD: 51 µm     720g      

      始封温度4 (51 µm)     85.0°C  Internal Method

AFFINITY™ PL 1880G

Polyolefin Plastomer

陶氏塑料                    

             热性能          额定值单位制      测试方法      

             维卡软化温度       86.0°C  ASTM D1525

             溶融温度（DSC）       99.0°C  Internal Method    

             光学性能      额定值单位制      测试方法      

             光泽度(20°, 50.8 µm)      141  ASTM D2457

             透明度(50.8 µm) 83.0 ASTM D1746

             雾度(50.8 µm)     1.1%       ASTM D1003

             挤出             额定值单位制                    

             熔体温度       209°C                

             挤压说明                           

             吹塑薄膜的制造条件：                           

                    •    螺杆尺寸：2.5英寸(63.5 mm)；24:1 L/D                          

                    •    螺杆类型：SFDM                     

                    •    模具间隙：70密尔(1.8 mm)                        

                    •    熔体温度：408°F (209°C)                          

                    •    输出：模具周长的6磅/小时/英寸                       

                    •    模具直径：6英寸                           

                    •    放大比：2.5:1                           

                    •    螺杆速度：50 rpm                           