Chemical composition

主要成份(%)

Characteristics & application

特性和用途

Equivalent to AWS

相当AWS

 

Hardfacing

 

 

 

 

S 101

C3 Cr28 Ni4
Si3.5 Fe Rem.

HRc48-54. Resistance to wear, gas corrosion and oxidation. Hardfacing of bucket tooth and case pump.
HRc48-54,耐磨、耐气蚀、抗氧化。堆焊铲斗齿,泵套

S 111

C1 Cr29 W5
Co Rem.

HRc38-47. Resistance to wear and corrosion at high-temperature. Hardfacing of high temperature and pressure valve.
HRc38-47,高温下耐磨、耐蚀。堆焊高温高压阀门

ECoCr-A

S 112

C1.5 Cr29 W8
Co Rem.

HRc45-50. Resistance to wear and corrosion at high-temperature. Hardfacing of valve and hot-rolling pass.
HRc45-50,高温下耐磨、耐蚀。堆焊阀门,热轧孔型

ECoCr-B

S 113

C2.5 Cr30 W17
Co Rem.

HRc55. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of screw charging carriage.
HRc55,高温下耐磨、耐热,但抗冲击性差。堆焊螺旋送料机用

S 114

C2.5 Cr30 W12
Co Rem.

HRc53. Wear and heat resistance at high temperature, bad shock resistance. Hardfacing of three-cone bit.
HRc53,高温下耐磨、耐热,但抗冲击较差。堆焊牙轮钻头

ECoCr-C

 

Copper

alloys

 

 

 

 

S 201

Sn1 Si0.3Mn0.3
Cu Rem.

Good mechanical properties and crack resistance. Gas welding and argon arc welding of red copper.
机械性能好,抗裂性好。紫铜气焊及氩弧焊用

ERCu

S 211

Si3 Mn1
Cu Rem.

Good mechanical properties. Argon arc welding of copper alloys and MIG brazing of steel.
机械性能好,铜合金氩弧焊及钢的MIG钎焊用

ERCuSi-Al

S 212

Sn5 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。铜合金氩弧焊及钢的堆焊用

ERCuSn-A

S 213

Sn8 Cu Rem.

Wear resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨性好。铜合金氩弧焊及钢的堆焊用

ERCuSn-C

S 214

Al7.5 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用

ERCuAl-A1

S 215

Al9 Cu Rem.

Wear and corrosion resistance. Argon arc welding of copper alloys and surfacing of steel.
耐磨、耐蚀。铜合金氩弧焊及钢的堆焊用

ERCuAl-A2

S 221

Cu60 Sn1 Si0.3
Zn Rem.

Melting point is about 890. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约890℃。黄铜气焊及碳弧焊用,也可钎焊铜、钢、铸铁

S 221F

Cu60 Sn1 Si 0.3
Zn Rem.

S221 welding rod cOAted with flux.
外涂焊剂的S221焊丝

S 222

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

Melting point is about 880. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约880℃。黄铜气焊及碳弧焊用,也可钎焊铜、钢、铸铁

RBCuZn-C

S 222F

Cu58Sn0.9Si0.1
Fe0.8 Zn Rem.

S222 welding rod coated with flux.
外涂焊剂的S222焊丝

RBCuZn-C

S 223

Cu59 Sn0.6
Zn Rem.

Melting point is about 900. Braze welding of copper, steel and cast iron.
熔点约900℃。铜、钢、铸铁钎焊用

RBCuZn-A

S 224

Cu62 Si0.5
Zn Rem.

Melting point is about 905. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点约905℃。黄铜气焊及碳弧焊用,也可钎焊铜、钢、铸铁

Copper
alloys

 

 

S 225

Cu48 Ni10
Zn Rem.

Melting point is about 935and high strength. Braze welding of steel, nickel and carbide alloys.
熔点约935℃。高强度,钎焊钢、镍及硬质合金

RBCuZn-D

S 225F

Cu48 Ni10
Zn Rem.

S225 welding rod coated with flux.
外涂焊剂的S225焊丝

RBCuZn-D

S 226

Cu60 Sn0.3
Si0.2 Zn Rem.

Melting point is about 900. Gas welding of brass, also braze welding of copper, steel and cast iron.
熔点约900℃。黄铜气焊用,也可钎焊铜、钢、铸铁

S 227

Cu58Sn0.9Ni0.5
Si0.1 Fe0.8
Zn Rem.

Melting point is about 880. Gas welding and carbon arc welding of brass, also braze welding of copper, steel and cast iron.
熔点880℃。黄铜气焊及碳弧焊用,也可钎焊铜、钢、铸铁

RBCuZn-B

S 229

Cu55 Ni6 Mn4
Zn

Melting point is about 920, high strength. Braze welding of steel, nickel and hard carbide.
熔点约920℃。高强度,钎焊钢、镍及硬质合金用

Aluminum alloys

 

 

 

S 301

Al99.5

Good ductility and corrosion resistance. Gas welding and argon arc welding of pure aluminum.
塑性好、耐蚀。纯铝气焊、氩弧焊用

ER1100

S 311

Si5 Al Rem.

Corrosion resistance, wide range of usage. Gas welding and argon arc welding of aluminum alloys other than high magnesium alloys.
抗裂性好,通用性大。铝合金气焊、氩弧焊用。不宜用高镁合金

ER4043

S 321

Mn1.3 Al Rem.

Good corrosion resistance, weldability and ductility. Gas welding and argon arc welding of aluminum alloys.
良好的耐蚀性、可焊性及塑性。铝合金气焊、氩弧焊用

S 331

Mg5 Mn0.4
Al Rem.

Corrosion resistance and high strength. Argon arc welding of aluminum alloys.
耐蚀,强度高。铝合金氩弧焊用

ER5183